Titanium IrO2-Ta2O5 coated ribbon anode for cathodic protection

1. Substrate& Coating

Titanium ASTM B265 Grade1

1)Composition

2)Coating: Mixed Metal Oxide


2. Spectification:

3. Accelerated Life

a) MMO Ribbon(NACE Standard TM0108-2008/Test condition: 1M Na₂SO₄   15000A/m²

b) Working Life: 50 years

c) Formula: Accelerated Current Output×Time ≥ Working  × Working Life

For Example:

15000A/m² ×120h   42mA/m×10^-3    ×50 years×365 days×24 hours

                       1m×6.35mm×10^-3×2

4. Application:

·In fine sandy loam

·Release Cl2 or O2, or both releases Cl2 and O2 environment

·Typically used for cathodic protection of the ground tank bottom and

reinforced concrete structure

5. Feature:

·Ribbon titanium anode is often used to make grid – pattern

·Can be used for cathodic protection anodeofall kinds of tank bottom

·Uniform current distribution

·Simple installation

·Having excellent performance and a good combination with the concrete,

when used in a reinforced concrete structure

·The anode zone spacing can be adjusted to achieve the required design life

6. Production Flow:

Raw material --- Shearing --- Machining --- Picking ----Automatic coating ---Inspection---Package

7. Main Export Markets:

• Asia

• Australasia

• Central/South America

• Eastern Europe

• Mid East/Africa

• North America

• Western Europe

8. Equipment

Ribbon Cutter machine

Automatic and Continuous RibbonFurnace

Accerlerate Life Test

Coating Thickness Test

9.Products:

                 Raw Materials

\

7. Engineering Pictures

MMO Ribbon Anode for Under tank Cathodic Protection