1.Used as electrode anode materials, including electrolytic manufacturing of chromic acid, perchlorate, electrolytic oxidation method to purify the wastewater to reduce COD

2.Electrolytic smelting metals,Due to Pbo2 coatedTi electrode is resistanttosulfuric acids, suitable for electrodeposition insoluble anode materials in Zinc, Copper, Nickel, Cobalt sulfate, etc

3.Oil and water separation

4.Zinc plating, passivation, waste recycling;

5.Cathode anticorrosion

6.Neutral electrolytedephosphorization

1.Good electrical conductivity, high hydrogen evolutionoverpotentiality, good catalytic property,corrosion preventive, stable chemical properties, high electrochemically, allow passing a large current

2.Chemical stability,a lot of oxidant and acid have no effect on anode

3.good corrosion preventive and long life time(Especially shows long life in sulfuric acid solution andOrganic electrolyte).

4.hardness, abrasion resistance, low cost,.

5.Dimensionalstability, small space between the electrodes in using process,to solve the traditional lead anodefracture problems in solid, liquid and gas environment

6.Green,not to pollutebath solution,high quality

7.Ti base can reusable

Current range

<5000A/m2

Temperature range

<80 ℃

Coating material

PbO2

Vitriol concentration

<30%

Coating thickness

0.2-0.5mm

pH about the environment

1-12

Shape

mesh, plates, tubes, rods, etc.